1) Compressive strength
| Direction | 200 MCI | 400 MCI |
A (minimum) | 15.0 MPa | 15.0 MPa |
B (minimum) | 1.5 MPa | 1.5 MPa |
C (minimum) | 0.2 MPa | 0.2 MPa |
Specimen dimensions 25.4 mm, length 25.4 mm from direction A, B and C,where
Speed: 1mm/min | ||
2) Porosity/water absorption
| Item | 200 MCI | 400 MCI |
Minimum | 18.6% | 17.8% |
Maximum | 23.4% | 20.7% |
Average (n>5 per lot) | 22.1% | 19.6% |
Total pore volume | 0.18-0.24 (cm3/g) | 0.18-0.24 (cm3/g) |
3) Bulk density
| 100 MCI | 0.46 g/cm3±15% |
200 MCI | 0.43 g/cm3±15% |
300 MCI | 0.50 g/cm3±15% |
400 MCI | 0.48 g/cm3±15% |
4) Coefficient of Thermal Expansion
| Item | 200 MCI | 400 MCI |
Heating rate | 5C/min, 20C…1000C | 5C/min, 20C…1000C |
Average | 1.5*10-6K-1 | 1.8*10-6K-1 |
5) Thermal Conductivity
1.5…1.6 W/mk at temperature25C…600C
6) Specific Heat Capacity
At:100C/200C/300C
800KJ/Kg950KJ/Kg2000KJ/Kg
7) Continuous High TemperatureDurability
Maximum shrinkage of length after 100 hours at 1200C
200MCI 400MCI
Maximum:0.5% 0.1%
8) High TemperatureStability
Maximum shrinkage after 100 hours at 1450C
200 MCI400MCI
Maximum2.0%2.5%
9) Gas Flow Resistance
Flow speed16m/s200 MCI400 MCI
Pressure drop {10-2mmAg/mm} 60130
10) Structural Integrity to Thermal Shock
(Cooling withwater)
Cracks start at approx. 800C
No destruction of ceramic bodiesuntil approx. 1180C
11) Softeningtemperature
Definition: temperature, at which the instantaneous rateof thermal
expansion is zero.
Procedure: analogous to coefficient of thermalexpansion;
determination with extrapolation.
| Item | Stoneware | Cordierite | Mullite- Cordierite | Mullite |
| SiO2 | 69~71 | 46~48 | 29~30 | 27~28 |
| Al2O3 | 18~20 | 34~37 | 68~69 | 70~71 |
| MgO | 0.15~0.20 | 7.00~7.50 | --- | --- |
| K2O.Na2O.CaO | 3.00~3.30 | 2.50~2.90 | 0.70~0.90 | 0.80~1.20 |
| Fe2O3 | 0.70~0.90 | 0.70~0.90 | 0.50~0.70 | 0.50~0. |
Type | Cells per square inch (CPSI) | Wall thickness mm | Channel width | Channel area | Free area | Inside surface area m2/liter | Approximate |
MC-26 | 400 | 0.17 | 1.10 | 1.210 | 75 | 2.728 | 480 |
MC-27 | 400 | 0.20 | 1.07 | 1.745 | 71 | 2.654 | 480 |
MC-28 |
Avaliable Dimension(mm) :Items Min Max length 37 150 width 37 150 height 12 25 Hot Produt :Type Dimension MJ-F-1 55*55*12.5 MJ-F-2 66*66*12.5 MF-F-3 ...
Physical Properties:1) Compressive strength Direction 200 MCI 400 MCI A (minimum) 15.0 MPa 15.0 MPa B (minimum) 1.5 MPa 1.5 MPa C (minimum) 0.2 MPa 0...
Ceramic Packings Brief Introduction Ceramic tower packings have great advantage of acid-& heat resistance. It can withstand almost all kinds of ...
Molecular sieves used for adsorption of water from air and liquids, as water molecules are both polar and very small. Molecular sieves will adsorb ...
Dimension & Properties:1 11mm*11 Square 200Cells 2 135mm*11 Square 280Cells 3 111mm*11 Square 520Cells 4 120mm*22 Square 300Cells
Physical Properties:Item Unit Target SiO2 % 46.00~48.00 Al2O3 % 32.00~34.00 MgO % 8.00~8.55 K2O.Na2O.CaO % 1.20~1.40 Fe2O3 % 1.50~1.60 Tio.Bao % 0.70...